Used In Metallurgy Thermal Insulation Material - 60060050mm

1. High desity:220+-10%, 2. High working temp:1000C, 3.100% no asbestos, 4.Low thermal conductivity:<=0.058w/m.k - details see: https://www.buildingsupplieshub.com/used-in-metallurgy-thermal-insulation-material-10025172

Place of Origin: Shandong China (Mainland)	Brand Name: lzsunshine	Model Number: 60060050mm	working temperature: 1000C
linear shrinkage: <=2%(1000C 6H)	Thermal conductivity(W/m.k): ≤0.050+0.00011T	Ignition loss(%): 5.7	Compressive strength(Mpa): ≥0.50
Flexural strength(Mpa): ≥0.30	Density(kg/m3): 180-380	Quality moisture content (%): ≤7.5	Fax: 00865352805233
Tel: 00865352805232

Used In Metallurgy Thermal Insulation Material

Production:

Calcium silicate board main content: MgO 0.1%, SiO2 47%, CaO 45% and other content. Calcium silicate board was mixed it an slurry blending tank, then pay-off to the reaction still after

Technical spec:

Item	HCS-220
Density(kg/m3)	180-380
Quality moisture content (%)	≤7.5
Compressive strength(Mpa)	≥0.50
Flexural strength(Mpa)	≥0.30
Thermal conductivity(W/m.k)	≤0.050+0.00011T
Work temperature °C	1100°C
Linear shrinkage (%)	≤1.50(1050°C,3nrs)
Ignition loss(%)	5.7

Packaging Detail:calcium silicate board packed with plastic bags in cartonThermal Insulation MaterialThermal Insulation Material On MetallurgyUsed In Metallurgy Thermal Insulation MaterialMetallurgy Thermal Insulation Material

Delivery Detail:15-20days after 30%TT deposit