Smooth side HDPE geomembrane - ty-0.75

Tianhai ASTM standard HDPE geomembrane is produced from high-grade polyethylene resin, high intensity, good UV resistance - details see: https://www.buildingsupplieshub.com/smooth-side-hdpe-geomembrane-10057721

Type: Geomembranes	Place of Origin: Shandong China (Mainland)	Brand Name: tianyan	Model Number: ty-0.75
Material: HDPE,LDPE,LLDPE,Virgin or Recycled resin	Keywords: Geomembrane	Color: black,white or be optional	Certificates: CE, ISO
Thickness: 0.2-2.5mm	Width: 2-10m	Standard: ASTM, GB	Function: Waterproof
Tensile strength: >27Mpa	Tensile elongation: >700%

Smooth side HDPE geomembrane

HDPE geomembrane

1)Thickness:0.75--3.00mm
2)Roll width:4-8m
3)Roll length:according to user's requirements

Tianhai smoothHDPE geomembraneis produced from high-grade polyethylene resin produced by foreign and domestic large petrochemical enterprises by three-layer pressing and plastic formation technology and double layer pressing and rolling technology. The company is the only enterprise that uses the two technologies to produce earthwork film in the same industry. The company has plastic formation experience for more than twenty years, makes close cooperation with earthwork builder, makes continuous innovation, seeks perfection, and makes great efforts in providing the most reliable products to the customers.

Smoothside HDPE geomembrane technical index of ASTM test GM 13 standard

No.	Item	Test Value
No.	Item	0.75mm	1.0 mm	1.25 mm	1.5 mm	2.0 mm	2.5 mm	3.0mm
1	Minimum Density(g/cm³)	0.939
2	Tensile Property
	Strength at yield,N/mm	11	15	18	22	29	37	44
	Strength at break ,N/mm	20	27	33	40	53	67	80
	Elongation at yield,%	12
	Elongation at break,%	700
3	Tear Resistance N	93	125	156	187	249	311	374
4	Puncture Resistance N	240	320	400	480	640	800	960
5	Stress Crack Resistance, hrs	300
6	Carbon Black Content, %	2.0-3.0
6	Carbon Black Dispersion	1 or 2
7	Standard OTI Min	100
7	High Pressure OTI Min	400
8	Impact Cold Crack at -70°C	Pass
9	Water vapor permeability (g.cm/cm2 .s.Pa)	≤1.0×10-13
10	Dimensional Stability (%)	±2