SA Quarry Grout - SA811

1)Suitable for most grouting applications, 2)Water-resistant, 3)For internal and external use, 4)For joints up to 10mm wide - details see: https://www.buildingsupplieshub.com/sa-quarry-grout-10082952

Place of Origin: Shanghai China (Mainland)	Brand Name: Shunan	Model Number: SA811	Usage: Joint Mortar
Type: Cement Mortar	Quality Management System: ISO9001:2008	Colors: White/Black	Size(kg): 25kg

Shunan brick grout

Introduction:

Grout is mixture of ordinary Portland cement,polymer re-dispersible emulsion powder matched with various functional additives and the different levels quartz sand,has excellent flexibility and hydrophobicity.It mainly applies to filling in the tiles stitches which formed by marble,granite and ceramic tiles decorating surface.the construction workability is good,operating conveniently,weathering resisting and anti-aging.is a kind of non-toxic,non-combustible green environmental protection building materials which has excellent comprehensive performance

Construction Methods:

1.stir the product evenly with clean water,water-lime ratio 0.23:1,the stirred mixture should be used up within 2 hours

2.the base wall should be smooth,tough and clean

3.Using quantity: 1 - 2.5 kgs/m2,depending on the flatness of the base coat

Note:

1.Environment temperature should above 5 ° during construction time,don't construct in the sun direct scorching

2.Use construction standard water to stir the materials on the spot,any other materials adding is prohibited

3.Do maintenance and protection work after construction finished,avoid collision and destroy

4.Please rinse the uncomfortable body caused by irregular contact promptly and take medical treatment if serious

5.Quality guarantee period: 6 months,note rainproof and moisture proof during transportation,keep dry in storage time

6.National standard: JC /T1004-2006

Technical Parameters:

items		index
abrasion resistance mm3		lower than2000
shrinkage value mm/m		lower than3.0
flexural tensile strength( MPa)	standard experimental condition	higher than2.50
flexural tensile strength( MPa)	ater freezing and thawing cycles	higher than2.50
compression strength( MPa)	standard experimental condition	higher than15.0
compression strength( MPa)	after freezing and thawing cycles	higher than15.0
water absorption(g)	30min	lower than5.0
water absorption(g)	240min	lower than10.0