pp siding wall panel - HS4

Specification building material, 1.Exterior WALL, 2.Stone Siding Panels, 3.Easy to install, 4.Nice Look, Recycle, Water proo - details see: https://www.buildingsupplieshub.com/pp-siding-wall-panel-10027834

Place of Origin: Zhejiang China (Mainland)	Brand Name: huazhijie	Model Number: HS4	Material: PP
Color: aviliable	packing: CTN	function: waterproof , fire-resistance

contact supplier for pp siding wall panel

siding wall panel : pictures

siding wall panel :Material:PP

2. Width: 8inch(20.32cm),10inch(25.4cm)

3. Thickness: 0.8mm,0.9mm,1.0mm

4. Length:1.14(also according to the customers need)

5. Packing Quantity:6pcs/CTN

6. Package: Carton

siding wall panel: building material features

1) The variety of colors and patterns (13 colors for your option)

2) High intensity, resist erosion, anti aging

3) UV product, Fireproof, waterproof, environmental friendly

4) Easy to install and clean

9. Application: decoration of the outside wall of villa, apartment and renewing of the old building etc.

siding wall panel :building material specification

Detect items	Index
Folding strength under the natural dampish state (Mpa)	11±2
Fold strength after be dipped in water for 24 hours Mpa	>8.5
Drying shrinkage	<0.06%
Tensile strength on the vertical plane Mpa	>0.5
Resistance to impact(500g hammer weight,12mm thick panel)	Dropping from 1100mm meter, and has no penetrating cracks
Anti-folding elastic modulus(Mpa)	>3000
Density(T/M3)	1.1-1.4
Thickness expansion coefficient(%)after being dipped in water for 24 hours	<1.5
Fire resistance	B1 level
Moisture content(%)	10±5
Clutching nail force	>600
Heat conductivity coefficient(w/m.k)	0.19(density 1200kg/m3
Surface water resistance	No change within 96 hours
Surface alkali fastness	No change within 48 hours
Surface washing fastness	>5000 times
Surface aging resistance	No change within 1000 hours
Contamination resistant	<15%
Sound insulation value	36dB(single panel)
Bend degree after water absorption	Bend less than 3mm after water absorption
Water absorption	25%
Bond strength in cyclic test under the damp condition N/mm2	>0.3
Thickness expansion rate after the cyclic test under the damp condition %	1.5%
Ultraviolet irradiation	>Has no change, no crusting,no peeling within250hours
-40°C	The size and surface do not change after being frozen
Distortion performance under the wind pressure	Third level (GB/T15225-94)
Anti seismic within the distortion performance in the plan	First level (GB/T18250-2000)