Polysulphide Sealant for Construction - YL P2-2

Polysulphide Sealant for Construction, 1.Excellent resistance to low and high temperature, 2.Very low water absorptio - details see: https://www.buildingsupplieshub.com/polysulphide-sealant-for-construction-10059825

Type: Other Earthwork Products	Place of Origin: China (Mainland)	Brand Name: YULONG	Model Number: YL P2-2
Item NAME: Polysulphide Sealant for Construction	Skin time: 15-60mins	Hardness, Shore A: 38

Polysulphide Sealant for Construction

1.Excellent resistance to low and high temperature
2.Very low water absorption

YULONG Polysulphide Sealant for Construction

YL P2-2

Polysulfidesare one of the older polymer technologies for the manufacture of high-performance sealants. Despite a decline in popularity, they continue to be used in many parts of the world.

Product Use:
1: Glue-coating before glue coping withered material surface cleaning, clean before coating. Otherwise, it will affect the adhesive seal.
2: Takes out A and B two components according to 10: 1 proportion to carry on the mix agitation to be even, achieves the achromatism.
3: Manual or mechanical operation must arrange a direction coating and put some pressure, prevent the air wrapped into.
4: Construction of the ambient temperature maintained at above 5 ° C

Storage:

Store all materials in unopened containers in a dry area.Protect from heat and direct sunshine

Colour:

Part A (Base): White

Part B (Curing Agent): Black and Grey

After Mixed: Black and Grey

Packing details:

1. Machine : A group were 300kg, B group were 30kg (barrels package)

2. Manual: (1). A group were 30kg, B component 3kg (barrels package) or Per buyer’s demand

TECHNICAL DATA SHEET

Item	Detail	Result
Aspect/Appearance	Base/Part A	White Paste
Aspect/Appearance	Curing Agent/Part B	Black Paste
Viscosity, Pa·s	Base/Part A	4,000
Viscosity, Pa·s	Curing Agent/Part B	800
Specific Gravity	Base/Part A	1.6
Specific Gravity	Curing Agent/Part B	1.5
Mixed Component A and Component B at 10:1 by weight,under the conditions of 23±2^oC and the R.H. of 50±5%,after 7days of curing
Application Temperature,°C	Value	5~45
Aspect/Appearance	As mixed	Black, Non-slump Paste
Working time ,min	Value	20~60
Tacking-Free time, min	Value	20~60
Service Temperature,°C	Value	-50 ~+100
Hardness, Shore A		38
Peel Strength ,MPa	Value	2.05
Tensile strength, MPa		0.8
Elongation ,%	At Break	174