molding silicon for concrete facade moulds - HY-630

molding silicon for concrete facade moulds, 1.high temperature, acid and alkali resistance, 2.reused many times - details see: https://www.buildingsupplieshub.com/molding-silicon-for-concrete-facade-moulds-10088107
Place of Origin: Guangdong China (Mainland)Brand Name: Hongye siliconeModel Number: HY-630Material: Other
Model: 630#Appearance: whiteMixing proportion of curing agent (%): 4%Operating time (mins 25 0C ): 30-50
Curing time(hours 25 0C): 4-5Hardness (A°): 30±2Density ( g/cm3): 1.08Elongation-break(%): ≥ 460
Viscosity (mPas -25 0C): 25000±2000Retractility(%): ≤0.25  
molding silicon for concrete facade moulds
contact supplier for molding silicon for concrete facade moulds


molding silicon for concrete facade moulds

Usage: Silicon rubber for concrete bricks,PU/poly resin, unsaturated resin, plaster, candles and gypsums crafts, toys, soap, statuary ,casting molds making,etc.

Model630#
Appearancewhite
Mixing proportion of curing agent (%)4%
Operating time (mins 250C )30-50
Curing time(hours250C)4-5
Hardness (A°)30±2
Density ( g/cm3)1.08
Viscosity (mPas -250C)25000±2000
Tensile-strength(kgf /cm2)≥49
Tear-strength (kgf /cm)≥33
Elongation-break(%)≥ 460
Retractility(%)≤0.25

USERS INSTRUCTION:

RTV—TWOmolding silicone rubber (silicon) and silicon are generally named as two-part room temperature sulfurated silicone rubber, which features an exceptional fluidity and good operability.When mixed with 4% to5%curing agent, they can still be operated within 50 minutes,but will be formed after 4-5 hours.With resistance to deformation, high temperature, acid and alkali, and expansion, silicon flexible molds are used for mold duplication and delicate mold making for poli crafts, resin crafts lighting and candle crafts.

This product is a white or red flowable liquid with a hardness of 22 to 50A° when cured. If large products and therefore multiple-piece molds are needed by customers, silicone rubber with higher hardness will be required for the molds. Conversely, soft silicon is indispensable for molds with complicated pattern and delicate details. The amount of curing agent admixture depends on the actual need of customers. More will be added for speedy drying and fast release and less when otherwise.


(Note:we do not recommend silicon oil. For special soft mold or molds with complex pattern or fine details, 5% to10%silicon oil can be added to condition the flexibility of the mold for convenience of release)

Curing agent and silicon proportion and reaction(Under room-temperature-25C):
1,Added with 2%of curing agent, silicon can still flow within 2.5 hours, mold can be released in 7-8 hours.
2,Added with 3%of curing agent, silicon can still flow within 100mins to 1 hours, mold can be released in 6-7 hours.
3,Added with 4%of curing agent, silicon can still flow within 60-70 minutes, mold can be released in 5-6 hours.
4,Added with 5%of curing agent, silicon can still flow wtithin 50 minutes, mold can be released in 4-5 hours.