Magnesite brick used for non-ferrous metallurgical - ZJZHMGe-6 ZJZHMGe-8 ZJZHMGe-9 ZJZHMGe-12 ZJZHMGe-1

1. with the ISO9001:2008 and have the patent, 2.free sample, 3.delivery prompt, 4.OEM is welcome - details see: https://www.buildingsupplieshub.com/magnesite-brick-used-for-non-ferrous-metallurgical-10082114
Place of Origin: Henan China (Mainland)Brand Name: ZHENJINModel Number: ZJZHMGe-6 ZJZHMGe-8 ZJZHMGe-9 ZJZHMGe-12 ZJZHMGe-16 ZJZHMGe-18Type: Concrete Bricks
Porosity: SolidSize: the standard or as per your requirementColor: Red,redFunction: Firebricks
Feature: Thin BricksTechnique: Autoclavedshape: brickworklife: over 1 year
chemical composition: MgO Cr2O3 SiO2apparent porosity %: ≤18cold crush strength (Mpa): ≥40Refractoriness under load (℃): ≥1680
thermal shock resistance (1100℃): ≥7   
Magnesite brick used for non-ferrous metallurgical
contact supplier for Magnesite brick used for non-ferrous metallurgical


Director Bonded Magnesia-Chrome Brick

The Physical & Chemical Index:

trademark

index

item

ZJZHMGe-6ZJZHMGe-8ZJZHMGe-9ZJZHMGe-12ZJZHMGe-16ZJZHMGe-18

Chemical composition

(%)

MgO

≥80≥75≥75≥ 65≥60≥60

Cr2O3

≥6≥8≥9≥12≥16≥20

SiO3

≤1.8≤1.8≤1.8≤2.5≤2.8≤2.8

Volume density

(g/cm3)

≥2.90≥2.95≥3.0≥3.0≥3.05≥3.10

Apparent porosity(%)

≤18≤17≤17≤17≤17≤17

Cold crushing strength

(MPa)

≥50≥50≥50≥50≥45≥45

Refractoriness under load(°C)

T0.6≥1600≥1650≥1700≥1700≥1700≥1700

Thermal shock resistance,time(1100°C,water-cooling)

≥4≥5≥7≥7≥7≥7

Feature:

  • High hot strength,
  • High refractoriness under load,
  • Good chemical resistance

Applicaton:

  • burning zone of cement rotary kiln,
  • glass furnace,
  • steel-making electric furnace,
  • converter, non-ferrous metal smelting furnace

The Certification & the Company Qualification:

the Tunnel Kilns:

the 36 New Distributing Bin and Dust Guard affect the quality & environmental protection:

The Modern Package Machine & the Finished Products:

the Company News:

It was released by Zhenjin refractories Co ., Ltd. recently that the magnesium aluminate spinel bricks for large scale cement rotary kiln which passed the achievement identification of Science and Technology Office of Henan

Province has been safely used in the 5000t /d cement production line of Huaxin Zigui Company for 6 months.

The spalling surface of the used magnesium aluminate spinel brick is smooth: the 200 mm thick brick only

spalled about 20 mm, and left 180-185 mm. it was estimated that the brick could serve

another 10 months, achieving good performance.

The ZHENJIN brand dominated brick:

Packaging Detail:wooden pallet + carton box + plastic bag
Delivery Detail:within 15 days after receive the deposit or the workable L/C

Related Product for Magnesite brick used for non-ferrous metallurgical