HM-180CE carbon fiber leaving adhesive - HM-180CE

Impregnation Adhesives for Carbon Fibre, 1.Modified epoxy resin, 2.Good penetration, 3.Low viscosity, 4.Water resistance - details see: https://www.buildingsupplieshub.com/hm-180ce-carbon-fiber-leaving-adhesive-10084551

Place of Origin: Shanghai China (Mainland)	Brand Name: HORSE	Model Number: HM-180CE	Components: A & B
Appearance of A & B: Thick Liquid	Mixing Ratio (Weight): A / B, 2 / 1	Operating Temperature: 5 ~ 40 ℃	Operable Time: > 30 min
Dry to Touch Time (20 ℃): 1 ~ 2 hrs	Curing Time (20℃): 3 ~7 days	Tensile Strength (Fully Cured): ≥ 40 MPa	Elastic Modulus (Fully Cured): ≥ 2500 MPa
Percentage of Elongation (Fully Cured): ≥ 1.5 %

contact supplier for HM-180CE carbon fiber leaving adhesive

HM-180C3P Modified Epoxy Resin Carbon Fiber Impregnation Adhesiveis used for impregnation and paste of reinforced component surface and fiber products.

It is completely impregnated in fiber products, and coheres fiber products effectively with the component surface, thereby to strengthen the components.

1. Product Characteristics

1) Good compatibility with carbon fiber.

2) Aging, water resistance and chemical corrosion resistance, excellent performance.

3) Low viscosity, can completely impregnated in fiber products.

4) The adhesive layer has excellent physical mechanical properties after curing, such as strong toughness and elasticity.

3. Working Performance

Slump (40°C)	2.0 mm
Operable Time (40°C)	> 60 min
Applicable Temperature	5 ~ 40 °C

4. Colloidal Performance

Compressive Strength	≥ 70.0 MPa
Tensile Strength	≥ 40.0 MPa
Bending Strength	≥ 50.0 MPa
Elastic Strength	≥ 2500 MPa

5. Bonding Capacity

Steel–steel Tensile Shear Strength	≥ 14 MPa
Pulling Bonding Strength along with Concrete	≥ 2.5 MPa

Packaging Detail:30 kilograms per set A net: 20 kilograms (Nor.) B net: 10 kilograms (Nor.) Other packing weight optional,according to customer's requests.

Delivery Detail:3 days after Payment