HM-180C3P High Strength Carbon Fiber Reinforced Adhesive - HM-180C3P

HM-180C3P High Strength Carbon Fiber Reinforced Adhesive 1.Modified epoxy resin, 2.Good penetration, 3.Low viscosity - details see: https://www.buildingsupplieshub.com/hm-180c3p-high-strength-carbon-fiber-reinforced-adhesive-10084407
Place of Origin: Shanghai China (Mainland)Brand Name: HorseModel Number: HM-180C3PComponents: A & B
Appearance of A & B: Thick LiquidMixing Ratio (Weight): A / B, 2 / 1Operating Temperature: 5 ~ 40 ℃Operable Time: > 30 min
Dry to Touch Time (20 ℃): 1 ~ 2 hrsCuring Time (20℃): 3 ~7 daysTensile Strength (Fully Cured): ≥ 40 MPaElastic Modulus (Fully Cured): ≥ 2500 MPa
Percentage of Elongation (Fully Cured): ≥ 1.5 %   
HM-180C3P High Strength Carbon Fiber Reinforced Adhesive
contact supplier for HM-180C3P High Strength Carbon Fiber Reinforced Adhesive


HM-180C3P High Strength Carbon Fiber Reinforced Adhesive is used for impregnation and paste of reinforced component surface and fiber products.

It is completely impregnated in fiber products, and coheres fiber products effectively with the component surface, thereby to strengthen the components.

1. Product Characteristics

1) Good compatibility with carbon fiber.

2) Aging, water resistance and chemical corrosion resistance, excellent performance.

3) Low viscosity, can completely impregnated in fiber products.

4) The adhesive layer has excellent physical mechanical properties after curing, such as strong toughness and elasticity.

2. Application Range

This product isepoxy fiber adhesiveof high performance, which is mainly used for the strengthening and reinforcement of buildings.

It can be used for the effective penetration bonding between many substrate materials and many fiber fabrics.

Substratescan be concrete, steel material, ceramic, stone, wood component, etc.

Fiber productscan be carbon fiber, glass fiber, basalt fiber, aramid fiber, etc.

3. Working Performance

Slump (40°C)2.0 mm
Operable Time (40°C)> 60 min
Applicable Temperature5 ~ 40 °C

4. Colloidal Performance

Compressive Strength≥ 70.0 MPa
Tensile Strength≥ 40.0 MPa
Bending Strength≥ 50.0 MPa
Elastic Strength≥ 2500 MPa

5. Bonding Capacity

Steel–steel Tensile Shear Strength≥ 14 MPa
Pulling Bonding Strength along with Concrete≥ 2.5 MPa

6. Usage Amount

The usage amount is 0.6-0.9 kg for a square meter of fiber cloth.

7. Package

30 kilograms per set. A net: 20 kilograms (Nor.) B net: 10 kilograms (Nor.)
Other packing weight is optional according to customer's requests.

Packaging Detail:30 kilograms per set A net: 20 kilograms (Nor.) B net: 10 kilograms (Nor.) Other packing weight optional,according to customer's requests.