HM-180C3P Carbon Fiber Impregnation Adhesive for Concrete Bonding - HM-180C3P
| Place of Origin: Shanghai China (Mainland) | Brand Name: Horse | Model Number: HM-180C3P | Components: A & B |
| Appearance of A & B: Thick Liquid | Mixing Ratio (Weight): A / B, 2 / 1 | Operating Temperature: 5 ~ 40 ℃ | Operable Time: > 30 min |
| Dry to Touch Time (20 ℃): 1 ~ 2 hrs | Curing Time (20℃): 3 ~7 days | Tensile Strength (Fully Cured): ≥ 40 MPa | Elastic Modulus (Fully Cured): ≥ 2500 MPa |
| Percentage of Elongation (Fully Cured): ≥ 1.5 % |
HM-180C3P Carbon Fiber Impregnation Adhesive for Concrete Bonding is used for impregnation and paste of reinforced component surface and fiber products.
It is completely impregnated in fiber products, and coheres fiber products effectively with the component surface, thereby to strengthen the components.
1. Product Characteristics
1) Good compatibility with carbon fiber.
2) Aging, water resistance and chemical corrosion resistance, excellent performance.
3) Low viscosity, can completely impregnated in fiber products.
4) The adhesive layer has excellent physical mechanical properties after curing, such as strong toughness and elasticity.
2. Application Range
This product isepoxy fiber adhesiveof high performance, which is mainly used for the strengthening and reinforcement of buildings.
It can be used for the effective penetration bonding between many substrate materials and many fiber fabrics.
Substratescan be concrete, steel material, ceramic, stone, wood component, etc.
Fiber productscan be carbon fiber, glass fiber, basalt fiber, aramid fiber, etc.
3. Working Performance
| Slump (40°C) | 2.0 mm |
| Operable Time (40°C) | > 60 min |
| Applicable Temperature | 5 ~ 40 °C |
4. Colloidal Performance
| Compressive Strength | ≥ 70.0 MPa |
| Tensile Strength | ≥ 40.0 MPa |
| Bending Strength | ≥ 50.0 MPa |
| Elastic Strength | ≥ 2500 MPa |
5. Bonding Capacity
| Steel–steel Tensile Shear Strength | ≥ 14 MPa |
| Pulling Bonding Strength along with Concrete | ≥ 2.5 MPa |
6. Usage Amount
The usage amount is 0.6-0.9 kg for a square meter of fiber cloth.
7. Package
30 kilograms per set. A net: 20 kilograms (Nor.) B net: 10 kilograms (Nor.)
Other packing weight is optional according to customer's requests.
| Packaging Detail:30 kilograms per set A net: 20 kilograms (Nor.) B net: 10 kilograms (Nor.) Other packing weight optional,according to customer's requests. |
| Delivery Detail:3 days after Payment |
Related Product for HM-180C3P Carbon Fiber Impregnation Adhesive for Concrete Bonding
Boston Blend Tile Strips
Boston Blend Strips is real, all natural Thin Stone Veneer that has been sawn and split for easy and seamless installation.
Sand Suppliers in Chennai
This sand is commonly utilized in various construction, buildings, bricks, etc.
Granite
Brazilian Granite Blocks, Granite Slabs and Granite Cut to Order
Concrete Molds. Ledgestone stone veneer profile.
Each concrete mold makes 2 square feet of designer grade ledgestone stone veneer at a time.
Concrete Molds. Natural Cut Ledgestone stone veneer profile.
Each concrete mold makes 2 square feet of designer grade natural cut ledgestone stone veneer at a time.
River Rock rubber molds to make stone veneer.
Each mold makes 2 square feet of designer grade River Rock stone veneer at a time.
Concrete spacer
Concrete Block: 40mm,50mm,55mm,65mm,75mmgavanized wire in the central of block
Concrete strength:60 MPA-120MPA
Bomanite Toppings System
Can refurbish old, wornout surfaces and turn them into new, exciting expanses of color, pattern and texture.
Bomanite Vertical System
A technology combined with lightweight-polymer-modified-mixture to enable workability in vertical surfaces.
Bomanite Custom Polishing System
One application, permanent results. Lustrous color, protected by a tight, beautiful sheen.
Bomanite Grasscrete System
A void structured concrete, a pervious pavement system.