High quality TPO Waterproof Membrane with 15-years experience - TPO-H

1.TPO waterproof membrane, 2.No pollution and long lifetime, 3.Hot welding., 4.Good tension strength, 5.ISO-9001 - details see: https://www.buildingsupplieshub.com/high-quality-tpo-waterproof-membrane-with-15-years-experience-10100258

Type: Waterproof Membrane	Place of Origin: Shandong China (Mainland)	Brand Name: SD	Model Number: TPO-H
color: any color you like	width: 2.0m	length: 20m	thickness: 0.5mm 1.0mm 1.2mm 1.5mm 20mm
tensile strength retention,%≥: 90	elongation retention,%≥: 90	cold bending: no craze at-40℃	sample size: A4
standard: GB	certificate: ISO-9001

High quality TPO Waterproof Membrane with 15-years experience

contact supplier for High quality TPO Waterproof Membrane with 15-years experience

TPO Waterproofing Membranes

non-homogeneous composite membrane (code H)

Products Description

The Thermoplastice Polyolefin (TPO) waterproof membranes are the most popular waterproof materials in the world at present. It’s thermoplastic elastomeric waterproof materials by adopting advanced polymerization together with squeeze technology,which perform well in mechanical properties, high tensile strength,oxidation-resistance and resistance to puncture.

Products Specification

Name	Thickness(mm)	Width(m)	Length(m)
TPO-H	0.5-2.0	2.1	≥20

Products Hall

Physical Properties tpo waterproof membrane

TPOPhysical Properties

Item			Specification
			H	L	P		G	GL
The resin thickness of Middle fabric, mm≥			—		0.40
Maximum tension,N/cm ≥			—	200	250		—	200
Tension strength,Mpa≥			12				12
Maximum tension elongation,%≥					15
Fracture elongation,%≥			500	250			400	200
Heat treatment size change rate%≤			2.0	1.0	0.5		0.1	0.1
Low temperature bend			-40°C No crack
Water tightness			0.3Mpa,2h, No seepage
Attack resistance			0.5kg·m,No seepage
Static charge resistance			—			20kg ,No seepage
Seam strip strength ,N/mm≥			4.0 or Membranes break			3.0
Right-angle tear strength,N/mm≥			60				60
Trapezoid tear strength N≥			—	300		450		350
Bibulous rate (70°C 168h),%		After soaking≤	4.0
		Air-cure later≥	-0.40
Heat aging (115°C)	Time		672h
	Appearance		No blister,flaw,delamination,coherence,hole
	Tensile strength retention,%≥		90
	Elongation rate of keeping,%≥		90
	Low temperature bend		-40°C, No crack
Chemistry resistance	Appearance		No blister,flaw,delamination,coherence,hole
	Tensile strength retention,%≥		90
	Elongation rate of keeping,%≥		90
	Low-temperature bending		-40°C, No crack
Artificial weather accelerated aging	Time		1500hb
	Appearance		No blister,flaw,delamination,coherence,hole
	Tensile strength retention%≥		90
	Elongation rate of keeping%≥		90
	Low temperature bend		-40°C ,No crack