HDPE anti-skid point geomembrane LDPE water-proof geomemberane

1.Point HDPE Geomembrane, 2.High friction, 3.Anti-seepage,anti-pollution,anti-skid function, 4.Easy for construction - details see: https://www.buildingsupplieshub.com/hdpe-anti-skid-point-geomembrane-ldpe-water-proof-geomemberane-10057586

Type: Geomembranes	Place of Origin: Hebei China (Mainland)	Material: HDPE	LENGTH: 50-100M
WIDTH: 4-8M

HDPE anti-skid point geomembrane

1.Description

Points evenly distributed with increased friction,and the appearance is very beautiful.The two sides of geomembrane can be hot melted together by different clour and meterials.Wcan sert right side of products according to geological conditions and project requirements.The product is producted by processing of hot-welt,extrude,press pre-long,extension in reasonable controlling,which increase products'tensile strength,abrasion resistance.It retains supior mechanical property and excellent elongation and stable chemical property of raw materials.And through adding functional agents in fixed proportion,which improved products's function of anti-acid&alkali and anti-corrosion.It's tensile streng 3 times higher than normal 1 textured geomembrane.

2.Features: High friction,anti-seepage,anti-pollution,anti-skid function,easy for construction.

3.Tyoical Application: Ideal materials in landfill,anti-seepage and anti-fouling project for separation,waterproofing and anti-pollution.

HDPE Geomembrane with point Specification(USA GRI-GM17 Standards)

No.	Value
No.	Value	0.75mm	1.00mm	1.25mm	1.50mm	2.00mm	2.50mm	3.00mm
1	Density (g/cm²)	0.939
2	Tensile Propeties
	Yield Strength(N/mm)	11	15	18	22	29	37	44
	Break Strength(N/mm)	8	10	13	16	21	26	32
	Yield Elongation %	12
	Break Elongation %	100
3	Tear Resistance/N	93	125	156	187	249	311	374
4	Puncture Resistance/N	200	267	333	400	534	667	800
5	Stress Crack Tesistance/h	300
6	Carbon Black
	Carbon Black Content %	2.0-3.0
	Carbon Black Dispersion	Carbon black dispersion(only near spherical agglomerates)for 10 different views 9 in categoried 1 or 2 and 1 in category 3
7	Oxidative Induction Time(OIT)
	Standard OIT/min	100
	High Pressure OIT/min	400
8	Oven Aging at 85°C
	Standard OIT-% retained after 90 days	55
	High pressure OIT-% retained after 90 days	80
9	UV Resistance
	Standard OIT retained after 1600 hrs	Not recommended since the high temperature of the Std-OIT test produces an unrealistic result for some of the antioxidants in the UV exposed samples
	High pressure OIT retained after 1600 hrs	50
10	Low tempreture impact brittle property at -70°C	Pass
11	Permeability g·cm/(cm²)·Pa	≤1.0×10^-13
12	Dimensional Stability/%	±2