1.0mm Blacke HDPE liner - RH-GM

1.HDPE Geomembrane liner, 2Material: HDPE, LDPE, LLDPE, PVC,EVA, 3.Thickness: 0.2 - 4.5 mm, 4.high quality, 5.fastest shipping - details see: https://www.buildingsupplieshub.com/1-0mm-blacke-hdpe-liner-10057640

Type: Geomembranes	Place of Origin: Shandong China (Mainland)	Brand Name: Ruiheng	Model Number: RH-GM
Material: HDPE,LDPE,LLDPE,PVC,EVA	Materials: HDPE,LDPE,LLDPE	Thickness: 0.2mm-4.0mm	Width: 1m-8m
color: white ,black,red,green,etc

contact supplier for 1.0mm Blacke HDPE liner

1.0mm Blacke HDPE liner is made from HDPE materials and granular product.

HDPE Smooth high-density polyethylene geomembrane
single-double side Textured high density polyethylene

geomembrane

Smooth HDPE Geomembrane
It is mainly used for waterproof and seepage-resistance for irragation ect

Smooth HDPE Geomembrane

Geomembranes are essentially impermeable lining materials used as fluid of containment barriers. Geomembranes have proven to befar more effectivethan traditional products such as concrete, asphalt and compacted clay. They display a wide range of physical, mechanical and chemical resistance properties and can becompounded for greater resistanceto ultraviolet light exposure, ozone and micro organisms.

Moreeconomical to install,geosynthetic containment systems areless susceptible to ground movementand are now considered thesafest methodin the majority of applications.

Geomembranes can be of polymeric or composite construction have smooth or textured surfaces. Textured surfaces provide enhanced friction characteristics which can be important in certain applications.

Item	Technical Data
Item	0.30	0.50	0.75	1.00	1.25	1.50	2.00
Density(g/cm3)	0.94+/-1
Yield Strength(N/mm)	4	7	10	13.5	16	20	26
Break Strength(N/mm	6	10	15	20	25	30	40
Yield Elongation(%)	11
Break Elongation(%)	525
Tearing Strength((N)	34	56	84	113	140	168	224
Puncture Resistance(N)	72	120	180	240	300	360	480
Stress Crack Resistance(h)	200
Carbon Content (%)	2.0
Carbon Dispersion	It is nine A or B grade and no more than one grade C during ten data
Oxidative Induction Time	60
-70°C Embitterment	Pass
Vapor Permeation	1.0X10-13(g.cm/cm2.s.pa)
Size Stability(%)	±2.0